Microstructure modifications of Al-Si-coated press-hardened steel 22MnB5 by laser welding
Šebestová, Hana; Horník, Petr; Mika, Filip; Mikmeková, Šárka; Ambrož, Ondřej; Mrňa, Libor
2024 - English
Weld microstructure depends on the characteristics of welded materials and parameters of welding technology, especially on the heat input that determines the peak temperature and the cooling rate. When the coated sheets are welded, the effect of the chemical composition of the coating must be also considered even though its thickness is only a few tens of microns. During 22MnB5+AlSi laser welding experiments, the ferrite-stabilizing elements of coating modified the weld metal microstructure. Ferrite appeared in a quenched weld metal. The rapid cooling rate accompanying welding with a focused beam limited the homogenization of the weld metal which resulted in the formation of ferritic bands in the regions rich in Si and especially in Al. On the other hand, a high level of homogenization was reached when welding with the defocused beam. The ferritic islands uniformly distributed in the weld metal were formed at 0.4 wt% and 1.6 wt% of Si and Al, respectively. The doubled heat input reduced the Al content to 0.7 wt% insufficient for the ferrite formation at still relatively high cooling rates. Predicting the distribution of ferrite in the weld metal is challenging due to its dependence on various factors, such as cooling rate and the volume of dissolved coating, which may vary with any modifications made to the welding parameters.
Keywords:
laser welding; high-strength steel; microstructure; heat input; ferrite stabilization
Available at various institutes of the ASCR
Microstructure modifications of Al-Si-coated press-hardened steel 22MnB5 by laser welding
Weld microstructure depends on the characteristics of welded materials and parameters of welding technology, especially on the heat input that determines the peak temperature and the cooling rate. ...
Influence of ball material on the resulting fatigue life of thermal sprayed HVOF coatings in dynamic impact testing
Duliškovič, J.; Daniel, Josef; Houdková, Š.
2024 - English
Dynamic impact wear, i.e. contact between two components in the presence of high cyclic local loads, is a challenging failure mode that occurs in many mechanical applications. Many previous studies have confirmed that dynamic impact testing is suitable for evaluating the contact fatigue of thermal sprayed coatings. However, the effect of the test parameters on the resulting lifetime is unclear. The aim of this study describes the effect of the ball material used in the dynamic impact test on the resulting fatigue life of the HVOF thermal sprayed coating. Three test balls made of WC/Co alloy, Si3N4 silicon nitride and 440 C steel were chosen for this study. Dynamic impaction testing was carried out on the Cr3C2-NiCr coating, which was sprayed by HVOF on a 1.2376 high-speed steel substrate. The impact lifetime was described by the number of critical impacts, i.e. the number of impacts before coating fatigue occurs. Furthermore, the depth and volume of impact craters were measured. Using scanning electron microscopy (SEM), the surface of the impacts as well as the microstructure of the coating on the cross-section in the region of the impacts were observed. Furthermore, the mechanism of crack propagation in the coating and the microstructure of the indentor were investigated.
Keywords:
dynamic impact test; HVOF; Cr3C2-NiCr; fatigue
Available at various institutes of the ASCR
Influence of ball material on the resulting fatigue life of thermal sprayed HVOF coatings in dynamic impact testing
Dynamic impact wear, i.e. contact between two components in the presence of high cyclic local loads, is a challenging failure mode that occurs in many mechanical applications. Many previous studies ...
Functional Tungsten-based thin films and their characterization
Košelová, Zuzana; Horáková, L.; Sobola, Dinara; Burda, Daniel; Knápek, Alexandr; Fohlerová, Z.
2024 - English
Anodizing is a technique by which thin oxide layers can be formed on a surface. Thin oxide layers have been found to be useful in a variety of applications, including emitters of electrons. Tungsten is still a common choice for cold field emitters in commercial microscopy applications. Its suitable quality can be further improved by thin film deposition. Not only the emission characteristic can be improved, but also the emitter operating time can be extended. Tungsten oxide is known for its excellent resistance to corrosion and chemical attack due to its stable crystal structure and strong chemical bonds between tungsten and oxygen atoms. Many techniques with different advantages and disadvantages have been used for this purpose. Anodization was chosen for this work because of the controllable uniform coverage of the material and its easy availability without the need for expensive complex equipment. The anodizing process involves applying an electrical potential to tungsten while it is immersed in an electrolyte solution. This creates a thin layer of tungsten oxide on the surface of the metal. The thickness and properties of the resulting oxide layer can be controlled by adjusting the anodization conditions, such as the electrolyte solution, voltage, and the duration of the process. In this work, H3PO4 was used as the electrolyte to test whether these tungsten oxide layers would be useful for electron emitters, for use in electron guns and other devices that require high-quality electron emitters. The properties were evaluated using appropriate techniques. In general, anodization of tungsten to form thin layers of tungsten oxide layers is a promising technique for producing high quality electron emitters.
Keywords:
cold-field emission; thin layer deposition; tungsten oxide; resonance enhanced tunneling; anodization
Available at various institutes of the ASCR
Functional Tungsten-based thin films and their characterization
Anodizing is a technique by which thin oxide layers can be formed on a surface. Thin oxide layers have been found to be useful in a variety of applications, including emitters of electrons. Tungsten ...
SMV-2023-30: ILA compact
Hrabina, Jan; Holá, Miroslava; Oulehla, Jindřich; Pokorný, Pavel; Lazar, Josef; Šarlejová, Tatiana; Šlechtický, Stanislav
2023 - Czech
Smluvní výzkum byl zaměřen na vývoj reference optického kmitočtů pro frekvenční stabilizaci kompaktních laserových zdrojů. Tato optická reference je založena na bázi absorpční kyvety plněných čistými plyny a dovoluje stabilizaci laserových zdrojů pomocí metod laserové spektroskopie. Kyveta je určena k použití jako reference optických kmitočtů laserové normály pracující v pásmu vlnových délek 532-633 nm. The contractual research was oriented towards the development of optical frequency reference intended for the frequency stabilisation of ultra-compact semiconductor laser sources. This optical reference is based on an absorption cell filled with ultra-pure absorption gases, and it allows precise locking of the lasers with laser spectroscopy methods. The cell will serve as a reference of optical frequencies in systems of laser standards (532-633 nm wavelengths).
Keywords:
absorption cell; iodine cell; laser spectroscopy; stabilised laser; frequency stability
Available at various institutes of the ASCR
SMV-2023-30: ILA compact
Smluvní výzkum byl zaměřen na vývoj reference optického kmitočtů pro frekvenční stabilizaci kompaktních laserových zdrojů. Tato optická reference je založena na bázi absorpční kyvety plněných čistými ...
SMV-2023-34: ULM2023
Hrabina, Jan; Holá, Miroslava; Oulehla, Jindřich; Pokorný, Pavel; Lazar, Josef; Šarlejová, Tatiana; Šlechtický, Stanislav
2023 - Czech
Smluvní výzkum byl zaměřen na vývoj reference optického kmitočtů pro frekvenční stabilizaci kompaktních laserových zdrojů. Tato optická reference je založena na bázi absorpční kyvety plněných čistými plyny a dovoluje stabilizaci laserových zdrojů pomocí metod laserové spektroskopie. Kyveta je určena k použití jako reference optických kmitočtů laserové normály pracující v pásmu vlnových délek 532-633 nm. The contractual research was oriented towards the development of optical frequency reference intended for the frequency stabilisation of ultra-compact semiconductor laser sources. This optical reference is based on an absorption cell filled with ultra-pure absorption gases, and it allows precise locking of the lasers with laser spectroscopy methods. The cell will serve as a reference of optical frequencies in systems of laser standards (532-633 nm wavelengths).
Keywords:
absorption cell; iodine cell; laser spectroscopy; stabilised laser; frequency stability
Available at various institutes of the ASCR
SMV-2023-34: ULM2023
Smluvní výzkum byl zaměřen na vývoj reference optického kmitočtů pro frekvenční stabilizaci kompaktních laserových zdrojů. Tato optická reference je založena na bázi absorpční kyvety plněných čistými ...
SMV-2023-35: NIM Víceprůchod
Hrabina, Jan; Holá, Miroslava; Oulehla, Jindřich; Pokorný, Pavel; Lazar, Josef; Šarlejová, Tatiana; Šlechtický, Stanislav
2023 - Czech
Smluvní výzkum byl zaměřen na vývoj referencí optických kmitočtů pro frekvenční stabilizaci kompaktních laserových zdrojů. Tyto optické reference jsou založeny na bázi absorpčních kyvet plněných čistými plyny a dovolují stabilizaci laserových zdrojů pomocí metod laserové spektroskopie. Kyvety jsou určené k použití jako reference optických kmitočtů pro laserové normály pracující v pásmu vlnových délek 532 nm. The contractual research was oriented towards the development of optical frequency references intended for the frequency stabilisation of ultra-compact laser sources. These optical references are based on absorption cells filled with ultra-pure absorption gases and they allow precise locking of the lasers with the methods of laser spectroscopy. The cells will serve as the references of optical frequencies in systems of laser standards (532 nm wavelengths).
Keywords:
absorption cell; iodine cell; laser spectroscopy; stabilised laser; frequency stability
Available at various institutes of the ASCR
SMV-2023-35: NIM Víceprůchod
Smluvní výzkum byl zaměřen na vývoj referencí optických kmitočtů pro frekvenční stabilizaci kompaktních laserových zdrojů. Tyto optické reference jsou založeny na bázi absorpčních kyvet plněných ...
SMV-2023-36: Wuhan Space
Hrabina, Jan; Holá, Miroslava; Oulehla, Jindřich; Pokorný, Pavel; Lazar, Josef; Šarlejová, Tatiana; Šlechtický, Stanislav
2023 - Czech
Smluvní výzkum byl zaměřen na vývoj reference optického kmitočtů pro frekvenční stabilizaci kompaktních laserových zdrojů. Tato optická reference je založena na bázi absorpční kyvety plněných čistými plyny a dovoluje stabilizaci laserových zdrojů pomocí metod laserové spektroskopie. Kyveta je určena k použití jako reference optických kmitočtů laserové normály pracující v pásmu vlnových délek 532-633 nm. The contractual research was oriented towards the development of optical frequency reference intended for the frequency stabilisation of ultra-compact semiconductor laser sources. This optical reference is based on an absorption cell filled with ultra-pure absorption gases, and it allows precise locking of the lasers with laser spectroscopy methods. The cell will serve as a reference of optical frequencies in systems of laser standards (532-633 nm wavelengths).
Keywords:
absorption cell; iodine cell; laser spectroscopy; stabilised laser; frequency stability
Available at various institutes of the ASCR
SMV-2023-36: Wuhan Space
Smluvní výzkum byl zaměřen na vývoj reference optického kmitočtů pro frekvenční stabilizaci kompaktních laserových zdrojů. Tato optická reference je založena na bázi absorpční kyvety plněných čistými ...
SMV-2023-01: Reliéfní struktury na principu diftraktivní optiky
Horáček, Miroslav; Kolařík, Vladimír; Matějka, Milan; Krátký, Stanislav; Chlumská, Jana; Meluzín, Petr; Král, Stanislav
2023 - Czech
Výzkum a vývoj v oblasti fyzikální realizace grafických a optických struktur na principu difraktivní optiky prostředky elektronové litografie v záznamovém materiálu neseném křemíkovou nebo skleněnou deskou. Výzkum zahrnuje analýzu grafického resp. optického motivu, výzkum a aplikaci reliéfních struktur realizujících požadované grafické resp. optické vlastnosti, výzkum a modelování možností fyzikální realizace reliéfních struktur, vypracování a analýzu technologie realizace reliéfní struktury s ohledem na limity současných vědeckých přístrojů, ověření teoretických úvah expozicí vzorku reliéfní struktury. Research and development in the field of physical realization of graphic and optical structures based on the principle of diffractive optics by means of electron beam lithography in a recording material supported by a silicon or glass board. The research covers the analysis of the graphical or optical motive, research and application of relief structures implementing the required graphic and optical properties, research and modeling of the physical possibilities of implementation of relief structures, preparation and analysis of technology of implementation of relief structures with regard to the limits of current scientific instruments, verification of theoretical considerations by means of relief structure sample exposure.
Keywords:
diffractive optical structures; relief structure; e-beam lithography
Available at various institutes of the ASCR
SMV-2023-01: Reliéfní struktury na principu diftraktivní optiky
Výzkum a vývoj v oblasti fyzikální realizace grafických a optických struktur na principu difraktivní optiky prostředky elektronové litografie v záznamovém materiálu neseném křemíkovou nebo skleněnou ...
SMV-2023-37: Projekt CRYSA - kryostat sondy 2
Frolec, Jiří
2023 - Czech
Cílem celého projektu CRYSA je výběr a testování tří kompozitních materiálů vhodných pro uchycení zařízení na velmi nízké teplotě (kryostatu), jež bude součástí chystané vesmírné sondy Athena od Evropské kosmické agentury (ESA). Na projektu spolupracuje skupina Kryogeniky a supravodivosti z Ústavu přístrojové techniky (ÚPT), firmy OHB Czechspace, 5M s.r.o. a Ústav fyziky materiálů AV ČR. Uvedené smluvní výzkumy se v r. 2023 v ÚPT zaměřily na dílčí cíle projektu. Konkrétně byl finalizován výběr tří nejlepších materiálů, které budou v budoucnu testovány, byly vypracovány detailní postupy pro plánované měření tepelných vodivostí vzorků a metoda jejich teplotního cyklování za nízkých teplot. Pracovníky skupiny Kryogenika a supravodivost byla také provedena optimalizace měřící aparatury a změřeny tepelné vodivosti několika cvičných vzorků. Výstupy tohoto projektu pomohou ESA s výběrem optimálního materiálu pro konstrukci závěsů uvedeného kryostatu pro dalekohled Athena. The goal of the project CRYSA is the selection and testing of three composite materials suitable for fixation of a low temperature device (cryostat), which will be part of the upcoming Athena space probe from the European Space Agency (ESA). The Cryogenics and Superconductivity group at the Institute of Scientific Instruments of the Czech Academy of Sciences (ISI Brno), OHB Czechspace, 5M s.r.o. and the Institute of Physics of Materials of the CAS (IPM) collaborate on this project. The aforementioned contractual researches carried out at ISI Brno in 2023 were focused on the partial goals of the project. Specifically, the selection of the three best materials, which will be tested in the future, was finalized. Further, detailed procedures for the planned measurements of the thermal conductivity of the samples and the method of their temperature cycling at low temperatures were developed. The members of the Cryogenics and Superconductivity Group also performed optimization of the measuring devices and measured thermal conductivities of several dummy samples. The outputs of this project will help ESA with the selection of the optimal material for the construction of the mechanical supports for the cryostat in the Athena telescope.
Keywords:
thermal conductivity; cryogenics; space probe; Athena
Available at various institutes of the ASCR
SMV-2023-37: Projekt CRYSA - kryostat sondy 2
Cílem celého projektu CRYSA je výběr a testování tří kompozitních materiálů vhodných pro uchycení zařízení na velmi nízké teplotě (kryostatu), jež bude součástí chystané vesmírné sondy Athena od ...
SMV-2023-03: Držák autoemisních katod
Knápek, Alexandr; Horáček, Miroslav; Klein, Pavel
2023 - Czech
Smluvní výzkum (SMV) se zabývá vývojem modulárního držáku pro vývoj a testování auto-emisních katod v podmínkách ultra-vysokého vakua. Výzkum kombinuje znalosti z vakuové techniky, silnoproudé elektrotechniky a povrchové fyziky k dosažení spolehlivého zařízení, které umožňuje pracovat s polně-emisními katodami ve vakuových podmínkách, a to v diodové a triodové konfiguraci. Hlavním výstupem pro objednavatele je výkresová dokumentace, která umožňuje aparaturu replikovat a dále jeden kus funkčního prototypu, který byl v rámci SMV zkonstruován k ověření funkcionality. The contract research (CR) deals with the development of a modular holder for the development and testing of field-emission cathodes under ultra-high vacuum conditions. The research combines knowledge from vacuum engineering, power electronics and surface physics to achieve a reliable device that allows working with field-emission cathodes under vacuum conditions in diode and triode configurations. The main deliverables for the customer are drawings that allow the apparatus to be replicated and one piece of working prototype that has been constructed within the CR to verify the function.
Keywords:
field-emission cathode holder; relief structure; modular holder
Available at various institutes of the ASCR
SMV-2023-03: Držák autoemisních katod
Smluvní výzkum (SMV) se zabývá vývojem modulárního držáku pro vývoj a testování auto-emisních katod v podmínkách ultra-vysokého vakua. Výzkum kombinuje znalosti z vakuové techniky, silnoproudé ...
NRGL provides central access to information on grey literature produced in the Czech Republic in the fields of science, research and education. You can find more information about grey literature and NRGL at service web
Send your suggestions and comments to nusl@techlib.cz
Provider
Other bases