Analysis of water soluble salts in bricks (Landštejn)
Ševčík, Radek
2020 - Czech The research report presents the results of water extracts analysis of bricks originated form Landštejn castle. The determination of chlorides, nitrates and sulphates was performed using ion chromatography. Výzkumná zpráva přináší výsledky analýz vodních výluhů z cihel pocházejících z hradu Landštejn. Metodou iontové chromatografie byl stanoven obsah chloridů. Keywords: salts; bricks; ion chromatography Available at various institutes of the ASCR Analysis of water soluble salts in bricks (Landštejn)

The research report presents the results of water extracts analysis of bricks originated form Landštejn castle. The determination of chlorides, nitrates and sulphates was performed using ion ...

Ševčík, Radek
Ústav teoretické a aplikované mechaniky, 2020

Analysis of stabilization of masonry walls on the Štamberk castle ruins
Drdácký, Miloš; Frankeová, Dita
2020 - Czech Analysis involves study of typology of individual phases of medieval stone masonry, classification of its quality, description of its condition and identification of its damage and failures. It suggests safeguarding and protection of masonry ruins including their presentation. It presents results of basic material characterisation of lime mortars on the castle. Analýza zahrnuje studium typologie jednotlivých fází středověkého kamenného zdiva, klasifikaci jeho kvality, popis jeho stavu a identifikaci poruch. Zabývá se návrhem záchrany zděných torz, jejich ochrany a prezentace. Uvádí výsledky základního testování materiálových charakteristik vápenných malt užívaných na hradu. Keywords: stone masonry; failures; damages; ruins; safeguarding Available at various institutes of the ASCR Analysis of stabilization of masonry walls on the Štamberk castle ruins

Analysis involves study of typology of individual phases of medieval stone masonry, classification of its quality, description of its condition and identification of its damage and failures. It ...

Drdácký, Miloš; Frankeová, Dita
Ústav teoretické a aplikované mechaniky, 2020

Survey of mortars of the Romanesque chapel in the tower of Landštejn Castle
Válek, Jan; Skružná, Olga; Kozlovcev, Petr; Frankeová, Dita; Svoboda, Milan; Ševčík, Radek; Kotková, Kristýna
2020 - Czech Four samples of floor mortars and two samples of plasters were analysed as a part of the survey in the Romanesque chapel located in the tower at Landštejn Castle. The aim was to characterize used raw materials, determine their ratio, characterize the porosity of mortars and compare mortars sorted to different phases of construction. V rámci průzkumu byly odebrány čtyři vzorky malt z podlahy a dva vzorky z omítek v prostoru románské kaple nacházející se ve věži na hradě Landštejn. Cílem byla charakterizace použitých surovin, stanovení jejich poměru, charakterizace porozity malt a porovnání malt z jednotlivých stavebních fází. Keywords: cultural heritage; Romanesque mortars; natural hydraulic lime; renders; floor mortars Available at various institutes of the ASCR Survey of mortars of the Romanesque chapel in the tower of Landštejn Castle

Four samples of floor mortars and two samples of plasters were analysed as a part of the survey in the Romanesque chapel located in the tower at Landštejn Castle. The aim was to characterize used raw ...

Válek, Jan; Skružná, Olga; Kozlovcev, Petr; Frankeová, Dita; Svoboda, Milan; Ševčík, Radek; Kotková, Kristýna
Ústav teoretické a aplikované mechaniky, 2020

Scientific report. Sps_025: Ceramics B4C + 1Ti, 1800°C, 2 min
Kumpová, Ivana; Vopálenský, Michal
2020 - Czech The aim of the measurement was to verify the feasibility of 3D computed tomography for observing structural details in samples of B4C - Ti ceramics with 1 % of Ti. Sample designated Sps_025: Keramika B4C + 1Ti, 1800°C, 2 min, in the form a cylinder with the diameter of 12 mm and the height of 10 mm was investigated by this method. Cílem práce bylo ověřit možnost pozorování stukturních detailů ve vzorcích B4C - Ti keramiky s 1 % titanu na základě 3D modelů z výpočetní tomografie. V laboratoři byl touto metodou zkoumán vzorek Sps_025: Keramika B4C + 1Ti, 1800°C, 2 min, ve tvaru válce o průměru 12 mm a výšce 10 mm. Keywords: X-ray tomography; boron carbide ceramics; characterization of microstructures Available at various institutes of the ASCR Scientific report. Sps_025: Ceramics B4C + 1Ti, 1800°C, 2 min

The aim of the measurement was to verify the feasibility of 3D computed tomography for observing structural details in samples of B4C - Ti ceramics with 1 % of Ti. Sample designated Sps_025: Keramika ...

Kumpová, Ivana; Vopálenský, Michal
Ústav teoretické a aplikované mechaniky, 2020

SEM-EDS characterization of building materials sampled from Slapy waterwork
Frankeová, Dita; Jurkovská, Lucie; Slížková, Zuzana
2020 - Czech Within the construction-technical survey framework, a microscopic analysis of historical concrete samples was performed using a scanning electron microscope and SEM-EDS analysis. Characterization of mortar components, determination of concrete degradation degree, and identification of chemical corrosion products. The results of the survey work were used as a basis for the reconstruction project. V rámci stavebně-technického průzkumu byl proveden mikroskopický rozbor vzorků historického betonu s využitím skenovacího elektronového mikroskopu a SEM‐EDS analýzy. Byla provedena charakterizace plniva a složek pojiva malt, určení stupně degradace betonu a identifikace produktů chemické koroze. Výsledky průzkumných prací byly použity jako podklad pro návrh rekonstrukce objektu.\n Keywords: waterwork; concrete; degradation Available at various institutes of the ASCR SEM-EDS characterization of building materials sampled from Slapy waterwork

Within the construction-technical survey framework, a microscopic analysis of historical concrete samples was performed using a scanning electron microscope and SEM-EDS analysis. Characterization of ...

Frankeová, Dita; Jurkovská, Lucie; Slížková, Zuzana
Ústav teoretické a aplikované mechaniky, 2020

Oak fastener in timber structures: materials for normative anchorage
Hasníková, Hana; Kunecký, Jiří; Hataj, M.; Tyrová, M.; Milch, J.; Suchomelová, P.
2019 - Czech Keywords: oak dowel; fastener; strength; stiffness; creep; mechanical behavior; destructive testing; variability Available at various institutes of the ASCR Oak fastener in timber structures: materials for normative anchorage

Hasníková, Hana; Kunecký, Jiří; Hataj, M.; Tyrová, M.; Milch, J.; Suchomelová, P.
Ústav teoretické a aplikované mechaniky, 2019

Chemical and microstructural characterization of the concrete and mortars sampled from the Klavary waterwork
Frankeová, Dita; Jurkovská, Lucie
2019 - Czech Within the framework of the construction-technical survey, a microscopic analysis of historical concrete samples was performed using a scanning electron microscope and SEM-EDS analysis. Characterization of mortar components, determination of concrete degradation degree and identification of chemical corrosion products. The results of the survey work were used as a basis for the reconstruction project. V rámci stavebně-technického průzkumu byl proveden mikroskopický rozbor vzorků historického betonu s využitím skenovacího elektronového mikroskopu a SEM‐EDS analýzy. Charakterizace plniva a složek pojiva malt, určení stupně degradace betonu a identifikace produktů chemické koroze. Výsledky průzkumných prací byly použity jako podklad pro návrh rekonstrukce objektu. Keywords: TGA; SEM/EDS; binder characterization Available at various institutes of the ASCR Chemical and microstructural characterization of the concrete and mortars sampled from the Klavary waterwork

Within the framework of the construction-technical survey, a microscopic analysis of historical concrete samples was performed using a scanning electron microscope and SEM-EDS analysis. ...

Frankeová, Dita; Jurkovská, Lucie
Ústav teoretické a aplikované mechaniky, 2019

Large-area scans of paintings with high resolution
Vopálenský, Michal; Kumpová, Ivana
2019 - Czech The aim of the measurement was to obtain the radiographs from historical paintings from the Faculty of Restoration of the University Pardubice. Due to the dimensions of the paintings (up to 90 x 110 cm) it was necessary to develop a suitable measurement procedure for successive scanning of the paintings in the TORATOM device. The resulting data are important for the planning of the restoration processes of the paintings and can help to discover otherwise invisible details, like underpaintings etc. Cílem měření bylo získat radiografická data z historických maleb, zapůjčených Fakultou restaurování Univerzity Pardubice. Vzhledem k rozměru obrazů (až 90 × 110 cm) bylo třeba vytvořit vhodnou měřicí proceduru pro postupné skenování pláten v zařízení TORATOM. Výsledná data mají význam pro plánování restaurátorských prací na obrazech a mohou pomoci odhalit jinak neviditelné detaily v malbách, např. podmalby apod. Keywords: large-area X-ray scanning; radiography of fine-art objects; restoration of paintings Available at various institutes of the ASCR Large-area scans of paintings with high resolution

The aim of the measurement was to obtain the radiographs from historical paintings from the Faculty of Restoration of the University Pardubice. Due to the dimensions of the paintings (up to 90 x 110 ...

Vopálenský, Michal; Kumpová, Ivana
Ústav teoretické a aplikované mechaniky, 2019

Fracture Parameters of AAAS composites with ceramic precursor
Šimonová, H.; Rozsypalová, I.; Kumpová, Ivana; Trčka, T.; Frantík, P.; Rovnaníková, P.; Keršner, Z.
2019 - Czech The paper deals with alkali-activated aluminosilicate composites based on ceramic precursors with respect to their characterization by fracture-mechanical parameters. Three composites made of brick dust as a precursor and alkaline activator with silicate modulus Ms = 1.0, 1.2 and 1.4 were investigated. After 28 days of maturation, specimens with nominal dimensions of 40 × 40 × 160 mm were provided by an initial notch to 1/3 of the body height in the middle of the span. At least 6 samples were tested from each composite. Specimens were subjected to three-point bending tests during which force vs. deflection at midspan (F–d) and force vs. crack mouth opening displacement (F–CMOD) diagrams were recorded. By processing these diagrams, the values of the static modulus of elasticity, the effective fracture toughness (including its initiating component) and the specific fracture energy were determined using the effective crack model, Work-of-Fracture method, and Double-K fracture model. After the fracture experiments had been performed, compressive strength values were determined for informational purposes from one part of each specimen that remained after testing. All evaluations included the determination of arithmetic means and standard deviations. To obtain information about the internal structure of composites before and after mechanical testing, the selected body was examined by micro-tomography. Tomographic measurements and image processing were performed for qualitative and quantitative evaluation of internal structure changes with an emphasis on the calculation of porosimetric parameters as well as visualization of the fracture process zone. The fractal dimension of fracture objects was determined. Příspěvek se zabývá alkalicky aktivovanými aluminosilikátovými kompozity na bázi keramických prekurzorů z hlediska charakterizace lomově-mechanickými parametry. Byly vyšetřovány tři kompozity, vyrobené z cihelného prachu jako prekurzoru a alkalického aktivátoru se silikátovým modulem Ms = 1,0, 1,2 a 1,4. Zkušební tělesa měla nominální rozměry 40 × 40 × 160 mm a byla po 28 dnech opatřena zářezy uprostřed rozpětí do 1/3 výšky těles. Z každého kompozitu bylo zkoušeno nejméně 6 vzorků. Tělesa byla podrobována testům v tříbodovém ohybu, při kterých byly zaznamenávány diagramy síla vs. průhyb uprostřed rozpětí a síla vs. otevření ústí trhliny. Po korekci těchto diagramů se s využitím modelu efektivní trhliny, metody lomové práce a modelu dvojí-K stanovily hodnoty statického modulu pružnosti, efektivní lomové houževnatosti (včetně její iniciační složky) a specifické lomové energie. Po lomových testech se vždy na jednom ze zlomků určovaly hodnoty informativní pevnosti v tlaku. Všechna vyhodnocení zahrnovala určení aritmetických průměrů a výběrových směrodatných odchylek. Pro získání informace o vnitřní struktuře kompozitů před mechanickým testováním a po něm bylo vybrané těleso zkoumáno pomocí mikro-tomografie. Tomografická měření a zpracování obrazu byla provedena pro kvalitativní a kvantitativní vyhodnocení změn vnitřní struktury s důrazem na výpočet porozimetrických parametrů a také vizualizace lomové procesní zóny. Byla stanovena fraktální dimenze objektů lomu. Keywords: alkali-activated aluminosilicate (AAAS); ceramic precursor; fracture test; force-displacement diagram; X-ray micro-tomography Available at various institutes of the ASCR Fracture Parameters of AAAS composites with ceramic precursor

The paper deals with alkali-activated aluminosilicate composites based on ceramic precursors with respect to their characterization by fracture-mechanical parameters. Three composites made of brick ...

Šimonová, H.; Rozsypalová, I.; Kumpová, Ivana; Trčka, T.; Frantík, P.; Rovnaníková, P.; Keršner, Z.
Ústav teoretické a aplikované mechaniky, 2019

Tomographical investigation of the historical metal bracelets
Kumpová, Ivana; Vopálenský, Michal
2019 - Czech The work was focused on the method definition for the investigation of historical metal artifacts employing the X-ray tomography. Two metal bracelets made of brass and plated with silver were investigated in the laboratory. The goal was to determine the technology of manufacturing and damages, possible also to visualize the silver layer. Práce byla zaměřena na vytvoření metodiky využívající rentgenové (RTG) tomografické zobrazování pro průzkumy historických artefaktů na bázi kovů. V laboratoři byly touto metodou zkoumány dva kovové náramky z mosazi s postříbřeným povrchem. Průzkum byl proveden za účelem odhalení technologie výroby a případných poškození, případně řešení napojení stříbrné vrstvy. Keywords: X-ray tomography; investigation of historical objects; metal artifacts Available at various institutes of the ASCR Tomographical investigation of the historical metal bracelets

The work was focused on the method definition for the investigation of historical metal artifacts employing the X-ray tomography. Two metal bracelets made of brass and plated with silver were ...

Kumpová, Ivana; Vopálenský, Michal
Ústav teoretické a aplikované mechaniky, 2019