PROPERTIES OF NANOCRYSTALLINE FE-NI PARTICLES PREPARED BY THERMAL REDUCTION OF OXALATE PRECURSORS
Švábenská, Eva; Roupcová, Pavla; Havlíček, Lubomír; Schneeweiss, Oldřich
2024 - English
Recent technological advancements require development of cost-effective and high-performance magnets \nwhich ideally do not contain rare earth metals or noble metals. The promising candidates are Fe-Ni-based \nalloys, in particular, the Fe50Ni50 L10 phase (tetrataenite), which has a great perspective for producing hard \nmagnetic materials. Our study explores a promising method for preparing nanoparticles of Fe-Ni alloy from an \niron-nickel oxalate precursor. The coprecipitation method was employed to prepare oxalate precursors, \nfollowed by controlled thermal decomposition in a reducing hydrogen atmosphere. The morphology and \nproperties of the resulting particles were analysed using scanning electron microscopy (SEM) coupled with \nenergy dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD), Mössbauer spectroscopy (MS), and \nmagnetic measurements.\nThe SEM analysis revealed that the particles have approximately cube-shaped unit cell morphology with a\nsize in a range of 1 - 2 μm. Upon annealing, the samples contain multiple phases with varying Fe-Ni content.\nMagnetic measurements confirmed the formation of magnetically suitable Fe-Ni phases in the samples after \nannealing. Mössbauer spectroscopy emerged as a highly effective method for characterizing individual phases \nof the Fe-Ni system.
Keywords:
Magnetic materials; thermal decomposition; Mössbauer spectroscopy
Available at various institutes of the ASCR
PROPERTIES OF NANOCRYSTALLINE FE-NI PARTICLES PREPARED BY THERMAL REDUCTION OF OXALATE PRECURSORS
Recent technological advancements require development of cost-effective and high-performance magnets \nwhich ideally do not contain rare earth metals or noble metals. The promising candidates are ...
Realizace víceúčelového měřícího systému pro (sub)terahertzovou elektronovou spinovou rezonanční spektroskopii
Šedivý, Matúš; Malik, Aamir Saeed; Epel, Boris; Vrba, Radimír
2024 - English
Electron spin resonance (also called electron paramagnetic resonance or just EPR) spectroscopy includes methods that investigate matter via unpaired electrons. One of the progressive EPR methods is the rapid scan, which allows one to observe the kinetics of chemical reactions. Moreover, recent developments of high-frequency components expand application of high-frequency EPR (HFEPR), that use sub terahertz and terahertz waves. This thesis deals with the connection of both paths into the frequency rapid scan (FRaScan) HFEPR spectrometer that was recently developed at CEITEC BUT. A brief introduction to the theoretical background of EPR is provided, followed by an overview of the HFEPR instrumentation. The practical part describes a technical solution for the spectrometer. The emphasis is on the implementation of software through which the spectrometer is controlled, and measurements are automated. Afterward are shown example measurements of solid state materials, namely vanadium doped silicon carbide (SiC:V), lithium phthalocyanine (LiPc), and crystal of 1,3-bisdiphenylene-2-phenylallyl (BDPA). The examples demonstrate the capabilities of the spectrometer to acquire multi-frequency continuous wave spectra and frequency-swept spectra with dependency on the temperature and orientation of the sample, as well as the frequency rapid scan spectra. Spektroskopie elektronové spinové rezonance (také nazývaná elektronová paramagnetická rezonance nebo jen EPR) zahrnuje metody, které zkoumají hmotu prostřednictvím nepárových elektronů. Jednou z progresivních metod EPR je rychlé skenování, které umožňuje pozorovat kinetiku chemických reakcí. Kromě toho nedávný vývoj vysokofrekvenčních součástkách rozšířil použití vysokofrekvenční EPR (HFEPR), které využívají sub-terahertzové až terahertzové vlny. Tato práce se zabývá propojením obou cest do HFEPR spektrometru s rychlým skenováním frekvencí (FRaScan), který byl nedávno vyvinut na CEITEC VUT. Na začátku je stručně uvedena základní teorie k EPR, následovaný přehledem přístrojového vybavení pro HFEPR. V praktické části je popsáno technické řešení spektrometru. Důraz je kladen na implementaci softwaru, pomocí kterého je spektrometr ovládán a měření jsou automatizována. Následně jsou ukázány příklady z měření pevných látek, konkrétně karbidu křemíku dopovaného vanadem (SiC:V), ftalocyaninu líthia (LiPc) a krystalu 1,3-bisdifenylen-2-fenylallylu (BDPA). Příklady demonstrují schopnosti spektrometru získat multifrekvenční vlnově spojitá EPR spektra a frekvenčně rozmítaná spektra v závislosti na teplotě a orientaci vzorku, a taky spektra pomocí rychlého skenování frekvencí
Keywords:
Elektronová spinová rezonance; spektroskopie; spektrometr; magnetická rezonance; vývoj; přístroj; měřící aparatura; prototyp; terahertzové vlny; prudký sken; defekty v krystalech; kvantový bit; karbid křemíku; software; LabVIEW; simulace; Electron-spin resonance; spectroscopy; spectrometer; magnetic resonance; development; instrument; experimental setup; prototype; terahertz beams; rapid scan; defects in crystals; qubit; silicon carbide; software; LabVIEW; simulation
Available in a digital repository NRGL
Realizace víceúčelového měřícího systému pro (sub)terahertzovou elektronovou spinovou rezonanční spektroskopii
Electron spin resonance (also called electron paramagnetic resonance or just EPR) spectroscopy includes methods that investigate matter via unpaired electrons. One of the progressive EPR methods is ...
Modification of cooling system for laboratory measurement of rotor blade vibration
Maturkanič, Dušan; Procházka, Pavel; Hodboď, Robert; Voronova, Evgeniya; Mekhalfia, Mohammed Lamine
2024 - English
Last year, the replacement of the turbine wheel model was completed in the Laboratory of Rotational Laser Vibrometry of the Institute of Thermomechanics AS CR, v.v.i. Based on previous experience and the expected higher operating load planned for the new wheel, the cooling system was modified at the same time. The paper describes the main effort in this direction and the results that clarify the previous damage of the measuring device.
Keywords:
blade; vibration; cooling system; measurement; laboratory
Available at various institutes of the ASCR
Modification of cooling system for laboratory measurement of rotor blade vibration
Last year, the replacement of the turbine wheel model was completed in the Laboratory of Rotational Laser Vibrometry of the Institute of Thermomechanics AS CR, v.v.i. Based on previous experience and ...
DYNAMICS OF MACHINES AND MECHANICAL SYSTEMS WITH INTERACTIONS : PROCEEDINGS DYMAMESI 2024
Zolotarev, Igor; Pešek, Luděk; Kozień, M. S.
2024 - English
The aim of the DYMAMESI is to facilitate the exchange of up to date information and knowledge among specialists in structural and multibody dynamics, in coupled interacting systems as aero-elasticity, hydro-elasticity, biomechanics, systems with feedbacks and mechatronics. In 2023 will be hosted by Cracow University of Technology, Institute of Applied Mechanics, Section of Dynamics of Systems.
Keywords:
dynamics; vibrations of mechanical systems; vibrodiagnostics; energy transformations
Available at various institutes of the ASCR
DYNAMICS OF MACHINES AND MECHANICAL SYSTEMS WITH INTERACTIONS : PROCEEDINGS DYMAMESI 2024
The aim of the DYMAMESI is to facilitate the exchange of up to date information and knowledge among specialists in structural and multibody dynamics, in coupled interacting systems as aero-elasticity, ...
Studium interakce rizikový kov – mikroplast
Sinčáková, Lenka; Řezáčová, Veronika; Doležalová Weissmannová, Helena
2024 - English
Microplastics are ubiqitous in the aquatic environmet and serve as a vector of wide range of contaminants, including heavy metals. This thesis aimed to examine the adsorption processes of five heavy metals (Pb, Hg, Zn, Cu and Cd) onto polyethylene terephtalate (PET), common river and sea pollutant. There has not been found a clear trend with regard to the influence of the size of the microplastics on the adsorption process. The salinity of the environment, on the other hand, has been found to have a profound impact on the adsorption process, with the observable decline of the adsorbed amounts in the environment with high ionic strength. The analysed heavy metals have been sorted in ascending order by its adsorption on PET as follows: Hg Mikroplasty, široko zastúpené vo vodnom prostredí, slúžia ako vektor širokej škály kontaminantov, vrátane ťažkých kovov. Táto práca sa zaoberá adsorpciou piatich ťažkých kovov (Pb, Hg, Zn, Cu and Cd) na polyetylén tereftalát (PET), rozšírený polutant riek a morí. Pokiaľ ide o vplyv veľkosti mikroplastov na proces adsorpcie, nebol zistený jasný trend. Salinita prostredia má značný vplyv na adsorpčný proces s pozorovateľným poklesom adsorbovaných množstiev v prostredí s vysokou iónovou silou. Analyzované ťažké kovy boli zoradené vzostupne podľa ich schopnosti adsorpcie na PET nasledovne: Hg
Keywords:
microplastics; MPs; polyethylene terephtalate; PET; heavy metals; HMs; pollution; Pb; Hg; Zn; Cu; Cd; adsorption; atomic absorption spectrometry; AAS; Fourier transform infrared spectrometry; FTIR; fresh water; sea water; Langmuir isotherm; Freundlich isotherm; Temkin isotherm; mikroplasty; MPs; polyetylén tereftalát; PET; ťažké kovy; HMs; znečistenie; Pb; Hg; Zn; Cu; Cd; adsorpcia; atómová absorpčná spektrometria; AAS; infračervená spektrometria s Fourierovou transformáciou; FTIR; sladká voda; morská voda; Langmuirova izoterma; Freundlichova izoterma; Temkinova izoterma
Available in a digital repository NRGL
Studium interakce rizikový kov – mikroplast
Microplastics are ubiqitous in the aquatic environmet and serve as a vector of wide range of contaminants, including heavy metals. This thesis aimed to examine the adsorption processes of five heavy ...
Studium biodegradace syntetických polyesterů
Guziurová, Pavlína; Sedláček, Petr; Obruča, Stanislav
2024 - English
This thesis investigates the degradation characteristics of polyester polymers (PBS with incorporated dilinoleic succinate in different %wt.) in simulated body fluids, revealing minor changes in properties. Bacterial degradation was also investigated and analysis shows more significant differences in Gel Permeation Chromatography (GPC) and scanning electron microscope (SEM) results. While abiotic degradation predominates, bacterial environments lead to higher degradation levels than simulated body fluids, suggesting potential applications in packaging or agriculture. However, lower sensitivity to abiotic degradation opens new possibilities for further research into exploring bacterial and enzymatic degradation mechanisms for environmentally sustainable alternatives across industries. Tato práce se zabývá degradačními vlastnostmi polyesterových polymerů (PBS s inkorporovaným dilinoleovým sukcinátem v různých hmotnostních procentech) v simulovaných tělních tekutinách a odhaluje menší změny vlastností. Byla zkoumána také bakteriální degradace a analýza ukazuje významnější rozdíly ve výsledcích gelové permeační chromatografie (GPC) a skenovacího elektronového mikroskopu (SEM). Zatímco převažuje abiotická degradace, bakteriální prostředí vede k vyšším úrovním degradace než simulované tělní tekutiny, což naznačuje potenciální využití v obalové technice nebo zemědělství. Nižší náchylnost na abiotickou degradaci však otevírá nové možnosti pro další výzkum mechanismů bakteriální a enzymatické degradace pro ekologicky udržitelné alternativy v různých průmyslových odvětvích.
Keywords:
Degradation; poly(butylene succinate); poly(butylene succinate)-(dilinoleic succinate); microbial degradation; Caldimonas thermodepolymerans; simulated body fluids; gastroenterological fluid; colonic fluid; Degradace; poly(butylene sukcinát); poly(butylene sukcinát)-(dilinoleát sukcinát); mikrobiální degradace; Caldimonas thermodepolymerans; simulované tělní tekutiny; žaludeční šťáva; střevní tekutina
Available in a digital repository NRGL
Studium biodegradace syntetických polyesterů
This thesis investigates the degradation characteristics of polyester polymers (PBS with incorporated dilinoleic succinate in different %wt.) in simulated body fluids, revealing minor changes in ...
Vliv kalcinovaných jílů na vlastnosti cementových past
Florian, Vojtěch; Šilerová, Iva; Šiler, Pavel
2024 - English
In this thesis we studied the effect of calcined clays on the properties of Portland cement. For many years clays and calcined clays have been the subject of many studies, the most commonly examined clays being kaolinite and calcined kaolinite. However, due to late economical turbulences, originally cheap materials, such as kaolinite, became more expensive. Due to the importance of this economic aspect, the materials mainly used in this thesis are materials that could be classified as waste materials. We studied samples of natural and synthetic clays acquired from the region around Brno Czech Republic, which is an area rich in clay deposits. Collected clays were analyzed, calcined, milled, and had their pozzolan activity measured. The recently authorized norm ČSN EN 197-5 allows for up to 65% of cement to be substituted with other materials such as clays, which is almost double the amount compared to the previous maximum of 35% substitution. For this reason, we prepared cement-clay mixtures containing up to 70% clay. It was found that cement-clay mixtures containing 60% clay substitution exhibited mechanical properties that were at worst comparable to the reference sample of pure Portland cement, but in some cases these mixtures exhibited better mechanical properties than the reference sample. Mixtures containing 30-40% clay generally had better mechanical properties compared to the reference sample. Out of all the studied materials, mixtures prepared from the clay obtained in an abandoned brickyard had the highest flexural strength. At the age of 28 days, the mixtures had up to 60% higher flexural strength than the reference sample. The highest compressive strength was exhibited in cement-clay mixtures prepared from glauconite clay. With increasing clay content the compressive strength decreased. At 90 days at 10% clay content the mixture had 60% higher compressive strength compared to the reference sample and at 60% clay content, the mixture had 26,5% higher compressive strength compared to the reference sample. The use of these cement-clay mixtures appears to be promising for the improvement of mechanical properties and economic and ecological aspects. These cement-clay mixtures could reduce carbon dioxide emissions while being cheaper than Portland cement. V této práci byl studován vliv kalcinovaných jílů na vlastnosti portlandského cementu. Jíly a jílové materiály jsou studovány již mnoho let, přičemž nejvíce studovaný jíl je kaolín a kalcinovaný kaolín. Avšak kvůli změnám ekonomické situace původně levné materiály, např kaolín, zdražily. Vzhledem k důležitosti ekonomické stránky byly v této práci používany primárně jílové materály, které by bylo možné považovat za odpadní. Studovali jsme směs přírodních a syntetických jílů získaných z okolí Brna v České Republice, což je region bohatý na ložiska jílů. Tyto jíly byly analyzovány, kalcinovány, pomlety a byla u nich změřena pucolánová aktivita. Nově schválená norma ČSN EN 197-5 povoluje až 65% náhradu cementu jinými materiály, např jíly, což je téměř dvojnásobek v porovnání s původní maximální náhradou 35 %. Z toho důvodu byly v této práci připraveny cementovo-jílové směsi s až 70% obsahem jílu. Bylo zjištěno, že cementovo-jílové směsi s 60% obsahem jílu vykazovaly mechanické vlastnosti přinejhorším srovnatelné s referenčním vzorkem portlandského cementu, v některých případech měly tyto směsi dokonce lepší mechanické vlastnosti. Směsi s obsahem jílu kolem 30-40 % měly všeobecně lepší mechanické vlastnosti než referenční vzorek. Ze studovaných materiálů měly směsi připravené z jílu z opuštěné cihelny nejlepší ohybovou pevnost. Při stáří 28 dní měly směsi až o 60% vyšší ohybovou pevnost než referenční vzorek. Nejvyšší tlakovou pevnost vykazovaly cementovo-jílové směsi připravené z glaukonitického jílu. S rostoucím obsahem jílu tlaková pevnost klesala. V 90 dnech při 10% obsahu jílu měla směs o 60 % vyšší pevnost než referenční vzorek. Při 60% obsahu jílu byla pevnost ve srovnání s referenčním vzorkem o 26,5 % vyšší. Použití těchto cementovo-jílových směsí se zdá být slibné díky dobrým mechanickým vlastnostem a z ekonomického a ekologického hlediska. Tyto cementovo-jílové směsi by mohly snížit emise oxidu uhličitého a zároveň být levnější než portlandský cement.
Keywords:
Clay; clay material; clay substitution; cement-clay mixture; Portland cement; pozzolan activity; Jíl; jílový materiál; jílová náhrada; cemento-jílová směs; portlandský cement; pucolánová aktivita
Available in a digital repository NRGL
Vliv kalcinovaných jílů na vlastnosti cementových past
In this thesis we studied the effect of calcined clays on the properties of Portland cement. For many years clays and calcined clays have been the subject of many studies, the most commonly examined ...
Materiály pro fotovoltaické neurostimulátory na bázi křemíkových fotodiod
Kunovský, Ondřej; Weiter, Martin; Glowacki, Eric Daniel
2024 - English
This thesis is focused on the possibilities of neurostimulators with wireless energy transfer, specifically it explores optical power transfer. Commonly used neurostimulators comprise battery-powered implantable pulse generators, and suffer from the problem of bulky batteries, accounting for more invasive surgery and requirement of periodic replacement. In this work, the alternative of photovoltaic power transfer is explored. Monocrystalline silicon photovoltaic diodes are modified and used as energy transducers. These diodes were cut into different sizes of active surface area, and they were connected into series or parallel connections. These photovoltaic cells were coupled with electrodes made from eight different materials and four different sizes to cover a wide range of possible neurostimulation applications. Next, a prototype photovoltaic stimulator consisting of flexible electrodes and a photovoltaic driver was fabricated. This prototype was successfully tested on small animal models, which they were Hirudo verbena and Locusta migratoria. This work characterizes a range of combinations of individual electrode sizes and materials with photovoltaic diodes for different light intensities and frequencies, creating a map of relevant parameters which can be used to design a prototype stimulator for a specific application. This work lays a foundation for further development of photovoltaic powered neurostimulators to enable novel experiments and one day maybe less invasive clinical devices. Tato práce je zaměřena na možnosti neurostimulátorů s bezdrátovým přenosem energie, konkrétně se zabývá přenosem energie pomocí světla. Běžně používané neurostimulátory zahrnují bateriově napájené implantovatelné pulzní generátory a trpí problémem objemných baterií, které vyžadují invazivnější operace a nutnost periodické výměny. V této práci je zkoumána alternativa přenosu energie s využitím fotovoltaických diod. Monokrystalické křemíkové fotovoltaické diody jsou modifikovány a používány pro přeměnu energie ze světelné na elektrickou. Tyto diody byly rozřezány na různé velikosti aktivních ploch a byly zapojeny do sériových nebo paralelních zapojení. Tyto fotovoltaické články byly spojeny s elektrodami vyrobenými z osmi různých materiálů a se čtyřmi různými velikostmi fotovoltaických diod, aby pokryly širokou škálu možných neurostimulačních aplikací. Dále byl vyroben prototyp fotovoltaického stimulátoru skládající se z flexibilních elektrod a fotovoltaické diody. Tento prototyp byl úspěšně testován na modelech malých zvířat, kterými byli Hirudo verbena a Locusta migratoria. Tato práce charakterizuje řadu kombinací jednotlivých velikostí a materiálů elektrod s fotovoltaickými diodami pro různé intenzity a frekvence světla a vytváří mapu relevantních parametrů, z nichž lze navrhnout prototyp stimulátoru pro konkrétní aplikaci. Tato práce pokládá základ pro další vývoj fotovoltaických neurostimulátorů, které umožní nové experimenty a jednoho dne možná méně invazivní klinická zařízení.
Keywords:
bioelectronics; neurostimulation; photovoltaics; wireless power transfer; microelectrodes; materials for stimulation electrodes; bioelektronika; neurostimulace; fotovoltaika; bezdrátový přenos energie; mikroelektrody; materiály pro stimulační elektrody
Available in a digital repository NRGL
Materiály pro fotovoltaické neurostimulátory na bázi křemíkových fotodiod
This thesis is focused on the possibilities of neurostimulators with wireless energy transfer, specifically it explores optical power transfer. Commonly used neurostimulators comprise battery-powered ...
Zlaté nanosystémy pro molekulární detekci biologických vzorků v povrchově zesílené Ramanově spektroskopii
Kebabová, Mona; Bernátová,, Silva; Samek, Ota
2024 - English
Sensitive and accurate detection of analytes or bacteria is a crucial step in identifying dangerous compounds or pathogens, whether in the medical field or food safety. Utilizing advanced methods such as Surface-Enhanced Raman Spectroscopy (SERS) would help with identifying bacteria or analytes with high sensitivity and accuracy. To optimize the method, the proposed master thesis concentrates on the synthesis and characterization of metal nanoparticles (NPs) that enhance Raman signal by localized plasmon resonance in SERS. Firstly, the recent approaches to the synthesis of plasmonic nanostructures are discussed. The main part of the experimental work consists of the synthesis of gold (Au) and silver (Ag) NPs and their characterization and use for analysis of chemical and biological samples by SERS. The NPs were used for the detection of dye molecules (rhodamine 6G and methylene blue), as well as the pathogenic bacteria Staphylococcus aureus and Escherichia coli, adsorbed on the surface of the synthesized NPs. Furthermore, a highly specific label-based sandwich immunoassay based on SERS signal of Raman reported linked to bacteria and NPs was replicated. This label-based method is a technique for the detection of a specific bacterial strain with the purpose of identifying the bacteria quickly and accurately. In principle, antibodies against specific bacteria were bound to the nanoparticle surface via an avidin-biotin affinity, allowing the bacteria (E. coli and S. aureus) to be captured. The prepared sandwich immunoassay is a precursor to highly accurate and rapid detection of bacteria, which I believe will be achieved in future steps. Citlivá a přesná detekce analytů nebo bakterií je klíčovým krokem při identifikaci nebezpečných sloučenin či patogenů, ať už v oblasti medicíny nebo bezpečnosti potravin. Využití pokročilých metod, jako je povrchově zesílená Ramanova spektroskopie (SERS), by pomohlo identifikovat bakterie nebo analyty s vysokou citlivostí a přesností. Tato diplomová práce zaměřuje na syntézu a charakterizaci kovových nanočástic (NČ) pro citlivou detekci bakterií pomocí SERS, přičemž NČ zvyšují Ramanův signál lokalizovanou plazmonovou rezonancí. Nejdříve jsou diskutovány nejnovější přístupy k syntéze plazmonických nanostruktur. Hlavní část experimentální práce tvoří syntéza zlatých (Au) a stříbrných (Ag) NČ, jejich charakterizace a využití pro analýzu chemických a biologických vzorků pomocí SERS. Nanočástice byly použity pro detekci molekul barviv (rhodamin 6G a methylenová modř), a patogenních bakterií Staphylococcus aureus a Escherichia coli, adsorbovaných na povrch syntetizovaných NČ. Dále byl replikován vysoce specifický sendvičový imunotest detekovatelný pomocí SERS. Tato metoda umožňuje rychlou a přesnou detekci patogenů. Na povrch nanočástic se pomocí interakce avidin-biotin vážou protilátky, které slouží k zachycení bakterií (E. coli a S. aureus). Ačkoli dílčí kroky protokolu byly úspešné, ověření funkce sendvičového imunotestu se doposud nezdařilo, pravděpodobně kvůli změnám v použitých chemikáliích a protilátkách. Kroky nezbytné k replikaci protokolu budou provedeny v budoucnu.
Keywords:
Surface-enhanced Raman spectroscopy; gold nanoparticles; silver nanoparticles; Raman spectroscopy; bacterial detection; Povrchově zesílená Ramanova spektroskopie; zlaté nanočástice; stříbrné nanočástice; Ramanova spektroskopie; detekce bakterií
Available in a digital repository NRGL
Zlaté nanosystémy pro molekulární detekci biologických vzorků v povrchově zesílené Ramanově spektroskopii
Sensitive and accurate detection of analytes or bacteria is a crucial step in identifying dangerous compounds or pathogens, whether in the medical field or food safety. Utilizing advanced methods such ...
Electrochemistry of Acetaminophen
Mikysek, T.; Ludvík, Jiří
2024 - English
The contribution is focused on electrochemical oxidation of acetaminophen mainly in non-aqueous media. The influence of various organic solvents as well as the pH effect is described herein. The redox properties of acetaminophen were studied by means of cyclic voltammetry, and rotating-disk voltammetry. We found that the protonation/deprotonation of acetaminophen acts as a ratedetermining step, where the stability of phenoxy radical intermediate plays an important role.
Keywords:
acetaminophen; phenacetine; voltammetry
Available on request at various institutes of the ASCR
Electrochemistry of Acetaminophen
The contribution is focused on electrochemical oxidation of acetaminophen mainly in non-aqueous media. The influence of various organic solvents as well as the pH effect is described herein. The redox ...
NRGL provides central access to information on grey literature produced in the Czech Republic in the fields of science, research and education. You can find more information about grey literature and NRGL at service web
Send your suggestions and comments to nusl@techlib.cz
Provider
Other bases